RODRUN LC-5050GM
液晶聚合物
UNITIKA Plastics Division
Technical Data
產品說明
Unitika Rodrun is a thermoplastics for percision injection classified into semi-aromatic liquid crystal polyesters (LCPs). LC-5000 series has a excellent moldability (high flow without flash, using a mold of low temperature) and precision (low warpage).
LC-5000 series are suitable for almost all dipping soldering conditions and partial reflow soldering (low warpage).
LCP has stiff molecular structure to form liquid crystal at molten stage. The archeological properties of low viscosity under shear stress gives high flow without flash problems. Rodrun which use a standard mold temperature of 40°C shows the rheological merit of LCP clearly.
Out shape of a LCP seem to be just like a normal plastics, however, the solid LCP consists of crystal and glasified liquid crystal. Rodrun has a low crystalinity in the mold. This property yields low shrinkage and low warpage. Rodrun is a suitable resin for precision parts.
總體
材料狀態 • 已商用：停售
資料 1 • Technical Datasheet (English)
UL Yellow Card 2 • E47924-239951
Search for UL Yellow Card • UNITIKA Plastics Division
• RODRUN
供貨地區 • 亞太地區
填料/增強材料 • 玻璃纖維增強材料, 50% 填料按重量
• 半結晶 • 良好的成型性能 • 氣體阻隔性
性能特點 • 低翹曲性 • 流動性高
• 收縮性低
• 低粘度 • 耐化學性良好
用途 • 工程配件
加工方法 • 注射成型
物理性能 額定值單位制 測試方法
比重 1.84g/cm³ ASTM D792
吸水率 (23°C, 24 hr) 0.010% ASTM D570
機械性能 額定值單位制 測試方法
抗張強度 (屈服, 3.20 mm) 137MPa ASTM D638
伸長率 (斷裂) 3.5% ASTM D638
彎曲模量 ASTM D790
1.60 mm 20600MPa
3.20 mm 15200MPa
彎曲強度 ASTM D790
屈服, 1.60 mm 206MPa
屈服, 3.20 mm 186MPa
沖擊性能 額定值單位制 測試方法
無缺口懸臂梁沖擊 88J/m ASTM D256
熱性能 額定值單位制 測試方法
熱變形溫度 ASTM D648
0.45 MPa, 未退火 250°C
1.8 MPa, 未退火 215°C
可燃性 額定值單位制 測試方法
UL 阻燃等級 UL 94
0.800 mm HB
3.20 mm V-0
注射 額定值單位制
干燥溫度 130°C
干燥時間 4.0hr
料筒溫度 120°C
1 / 3 文件號： TDS-120038-zh
RODRUN LC-5050GM
液晶聚合物
UNITIKA Plastics Division
注射 額定值單位制
螺筒后部溫度 270°C
螺筒中部溫度 280°C
螺筒前部溫度 290°C
射嘴溫度 290°C
模具溫度 40.0°C
|