PEXIDAN® L/T-UV
高密度聚乙烯
SACO AEI Polymers
Technical Data
產品說明
High density moisture-curable PE compound for hot & cold water plumbing pipe. Suitable for DR 9 pipe applications in continuous service at operating conditions of 140°F and 80 psi.
PEXIDAN® L/T (including L/T-UV and L/T Eclipse) is a high density PEX system consisting of a silane grafted base compound A-1001 and a catalyst masterbatch CAT-003 (or A-1022 and CAT-117). When mixed and extruded in the proper proportions, the two-component system results in a material that is crosslinkable by exposure to moisture or by immersion in hot water at 90-95°C. PEXIDAN® L/T is listed by NSF International to standards 14 and 61 and to Canadian Standards Association standard B137.5. NSFI certification to ASTM F876 and ASTM F2023 testifies to its superior resistance to oxidation by hot, chlorinated water. PEXIDAN® L/T is permitted to be used in domestic continuous re-circulation systems and is listed by NSF as a NSF-pw CL5 / PEX 5006 material.
總覽
材料狀態 • 已商用：當前有效
資料 1 • Technical Datasheet (English)
搜索 UL 黃卡 • SACO AEI Polymers
供貨地區 • 北美洲 • 拉丁美洲 • 亞太地區
• 非洲和中東 • 歐洲
特性 • 高密度 • 抗氧化 • 可交聯
用途 • 管道系統
機構評級 • ASTM F2023 • CSA B137.5 • NSF 61
• ASTM F876 • NSF 14
形式 • 粒子
加工方法 • 管路擠出成型 • 擠出
物理性能 額定值(英制) 額定值(公制) 測試方法
密度 / 比重 3 0.948 0.946g/cm³ ASTM D792
熔流率（熔體流動速率） (190°C/2.16 kg) 0.70g/10 min 0.70g/10 min ASTM D1238
交叉結合的程度 70% 70% ASTM D2765
機械性能 額定值(英制) 額定值(公制) 測試方法
拉伸模量 ISO 527-1
-40°F (-40°C) 335000psi 2310MPa
32°F (0°C) 245000psi 1690MPa
73°F (23°C) 125000psi 862MPa
抗張強度 ASTM D638
屈服, 73°F (23°C) 3100psi 21.4MPa
屈服, 180°F (82°C) 1630psi 11.2MPa
屈服, 199°F (93°C) 1260psi 8.69MPa
斷裂, 73°F (23°C) 3430psi 23.6MPa
斷裂, 180°F (82°C) 1740psi 12.0MPa
斷裂, 199°F (93°C) 1740psi 12.0MPa
伸長率 ASTM D638
屈服, 73°F (23°C) 9.0% 9.0%
屈服, 180°F (82°C) 12% 12%
屈服, 199°F (93°C) 14% 14%
斷裂, 73°F (23°C) 240% 240%
斷裂, 180°F (82°C) 200% 200%
斷裂, 199°F (93°C) 240% 240%
彎曲模量 ISO 178
-40°F (-40°C) 75000psi 517MPa
32°F (0°C) 55000psi 379MPa
73°F (23°C) 30000psi 207MPa
PEXIDAN® L/T-UV
高密度聚乙烯
SACO AEI Polymers
機械性能 額定值(英制) 額定值(公制) 測試方法
流體靜力學設計基礎 - @ 68% DOC ASTM D2837
73°F (23°C) 1250psi 8.62MPa
180°F (82°C) 800psi 5.52MPa
200°F (93°C) 630psi 4.34MPa
熱性能 額定值(英制) 額定值(公制) 測試方法
維卡軟化溫度 255°F 124°C ASTM D1525
線形熱膨脹系數 - 流動 8.3E-5in/in/°F 1.5E-4cm/cm/°C ASTM D696
(-148 到 185°F (-100 到 85°C))
比熱 (73°F (23°C)) 0.459Btu/lb/°F 1920J/kg/°C
氧感應時間 (428°F (220°C)) > 50min > 50min ASTM D3895
補充信息 額定值(英制) 額定值(公制) 測試方法
Hot Elongation 4 內部方法
elongation under load : 302°F (150°C) 30% 30%
permanent elongation (set) after cooling : 0.0% 0.0%
302°F (150°C)
擠出 額定值(英制) 額定值(公制)
料筒 1 區溫度 320 到 350°F 160 到 177°C
料筒 2 區溫度 320 到 350°F 160 到 177°C
料筒 3 區溫度 320 到 350°F 160 到 177°C
料筒 4 區溫度 320 到 350°F 160 到 177°C
料筒 5 區溫度 365°F 185°C
口模溫度 365°F 185°C